Polyether Polyol Manufacturing Process

 Synthesis of DMC-based polyether polyol by a continuous method

 

A certain amount of DMC catalyst is taken and uniformly dispersed in a certain amount of small molecule initiator. Add 0.5 kg of the mixture of the initiator in the small test reactor. The vacuum was replaced 1-2 times with N2, and the N2 pressure was maintained at 0.1 MPa. After heating, stirring and raising the temperature to a certain temperature, the quantitative PO was introduced into the continuous autoclave with nitrogen gas for induction. When the induction is successful (the temperature in the kettle rises and the pressure drops), the PO is continuously passed to carry out the reaction. Open the outer loop and continue to pass the PO into the continuous kettle.

 

When the liquid in the reaction vessel is full, the PO, DMC catalyst and the initiator are continuously added to the kettle at a certain ratio and a certain speed through the power system. Continuous discharge is started when a certain pressure is reached in the continuous autoclave. Keep the feed rate the same as the discharge rate until all the stock is added. The crude product discharged from the kettle enters the aging kettle, and is heated, matured, degassed, and discharged to obtain a finished product.

 

As one of the polyether polyol manufacturers, NCMC has been developing and focusing on chemicals for more than 60 years, and now is one of the largest professional chemical suppliers in Jiangsu province, with the privilege authorized by China government for operation of hazardous chemicals, highly toxic chemicals, precursor and explosive chemicals.


 

Labels:

Comments

Post a Comment

Popular posts from this blog

Difference Between Sodium Laureth Sulfate And Sodium Lauryl Sulfate

Sodium laureth ether sulfate  (SLS) and sodium lauryl ether sulfate (SLES) are surfactants that play a role in foaming products. It is widely believed that the foam produced by a product is its performance. The composition of SLS and SLES reduces the surface tension of water. They can also be used as dispersants to properly mix spices and body spray. SLS and SLES can also be used in a variety of personal care products such as soap, shampoo, shower gel, toothpaste and other foaming products. SLS and SLES are also added to moisturizing lotions and sunscreens because of these properties. The difference between SLS and SLES is in the manufacturing process. SLS undergo a process called ethoxylation. And then you get SLES. Why do we have this ethoxylation process? Because SLS has some mild irritation on the skin, such as dry. The manufactured SLES are more gentle and do not irritate the skin. Many manufacturers do not use SLS because it is irritating. SLES should be softer o...
Post a Comment
Read more

Difference Between Sulfate And Sulfonate In Shampoo

  Sulfates and sulfonates have two things in common. First, they're all anionic surfactants. Second, they are often used for personal care applications. But there are many differences. They have different molecular mechanisms. They have different functions and they have different raw materials.   Sulfates Sulfate is a compound. It has carbon bonds and oxygen and sulfur bonds. They include substances such as sodium lauryl sulfate and sodium lauryl ether sulfate.   At low pH, these substances plus the c-o-s bond hydrolyze to produce alcohol and inorganic sulfate. At a high pH, sulfate is stable in the base and, if ethoxylated to a relatively high level, produces a low-foaming alkali-soluble surfactant. Sulphates can be prepared by reaction of fatty alcohol or fatty alcohol ethoxylates with reagents such as SO3 or chlorosulfonic acid (CSA).   The reason shampoo becomes thick foam in the shower is that it contains sulfate. Most shampoos and household cleansers contain su...
Post a Comment
Read more

What Are the Advantages of DMC Catalyst?

DMC catalyst is a new type of high-performance catalytic olefin oxide ring-opening polymerization catalyst, suitable for synthesis of olefin oxide polyether containing 1-6 functional groups. DMC catalyst manufacturers usually use low molecular weight organic complexing agents. The complexing agents beneficially affect the activity of the catalyst for epoxide polymerization. The production of polyether with DMC catalyst has the following advantages: Low production and running costs 1) No post-processing process and faster reaction speed increase the production capacity of the device by several times. 2) No post-treatment process reduces equipment investment, unit product energy consumption and water consumption, unit product solid waste and waste water production, and improves product yield. 3) It can produce higher molecular weight products with molecular weight of more than 2000 per mole of hydroxyl group. 4) The produced polyether has the characteristics of narrow molecular weigh...
Post a Comment
Read more