Polyether Polyol 8000

Product Name: Polyether Polyol 8000

Chemical Formula: N/A

Polyether Polyol CAS Number .: N/A

Dangerous Grade: NO

Technical Data of Polyether Polyol 8000

ITEMS	SPECIFICATION
Appearance	Transparent
Colority(APHA)	≤50
Hydroxyl value(KOH mg/g)	14±1.5
Viscosity(mPa·s, 25℃)	2000-4000
Water content(%)	≤0.05
Acid value(KOH mg/g)	≤0.08
PH value	5-8

Package and Storage:

200kg/drum or 1000kg/IBC drum

Store in a cool, dry place. Keep container closed when not in use

Application /Application Industries:

PU foams

The polyether polyols with their molecular weight 6000—20000 have the properties of low viscosity, and narrow molecular weight distribution relatively with so high molecular weight. Our company can produce the polyether polyols according to the requirement of customers.

High flash point, flammable. Explosion: no explosion. Use foam, powder, steam and water to put out when it is Firing. Toxicity: almost nonpoisonous. If the products splash on the skin or in the eyes, it must be washed immediately with plenty of water or go to see the doctor.

The products are stored in ventilated and dry warehouse storage at Room temperature. The period of storage is a year. If the specifications are good, it can be used again after a year. Prevent them from rain and relief lightly in transportation. Be sure not to turn upside down. Steel drums with zinc-plated which weight is 200kg.

As one of polyether polyol suppliers, we also have types of DMC Catalyst for sale, if you have needs, please contact us.

Comments

Difference Between Sulfate And Sulfonate In Shampoo

Sulfates and sulfonates have two things in common. First, they're all anionic surfactants. Second, they are often used for personal care applications. But there are many differences. They have different molecular mechanisms. They have different functions and they have different raw materials. Sulfates Sulfate is a compound. It has carbon bonds and oxygen and sulfur bonds. They include substances such as sodium lauryl sulfate and sodium lauryl ether sulfate. At low pH, these substances plus the c-o-s bond hydrolyze to produce alcohol and inorganic sulfate. At a high pH, sulfate is stable in the base and, if ethoxylated to a relatively high level, produces a low-foaming alkali-soluble surfactant. Sulphates can be prepared by reaction of fatty alcohol or fatty alcohol ethoxylates with reagents such as SO3 or chlorosulfonic acid (CSA). The reason shampoo becomes thick foam in the shower is that it contains sulfate. Most shampoos and household cleansers contain su...

What is Polyether Polyol

Polyether polyol is prepared by ring-opening polymerization of epoxide monomers (such as ethylene oxide, propylene oxide and 1,2-epoxybutane) and a compound containing two or more active hydrogen atoms (called an initiator). In the presence of alkali catalyst, active hydrogen compounds initiate ring opening and oxide addition will continue until the required molecular weight is obtained. The number of hydroxyl groups in polyether polyol is determined by the number of unstable hydrogen atoms in the initiator. If the initiator has two active hydrogen, glycol will be formed. The reactivity of polyether polyol to isocyanates depends on the initiator and the type of epoxy monomer that ends the ring-opening polymerization. The primary hydroxyl produced by polyol capped with ethylene oxide is more reactive than the secondary hydroxyl produced by propylene oxide, which is ideal for applications requiring rapid curing time. However, the use of initiator based on ethylene oxide and a...

What is Expandable Microsphere?

Brief Introduction of Expandable Microsphere The color of the expandable microspheres is white. Its average particle size is 10-30 μ m. Its average density is about 1100 kg / m 3 . It has a thermoplastic shell comprising a low boiling liquid hydrocarbon. When the thermoplastic shell is softened at elevated temperatures, the increased pressure of the hydrocarbon will cause the microspheres to expand 40 to 100 times. When the internal pressure of the microsphere, the shell tension and the external pressure reach equilibrium, the microspheres no longer expand. Expandable microspheres have become the world's lightest application because the density of expanded microspheres is less than 30 kg / m3 (0.03 g / cm3). Characteristics of Expandable Microsphere The first feature is cost savings. In thermoplastic materials such as PR, PP, PVC, PET, TPR, TPU, TPV, PA and paper/paperboard, expandable microspheres can be used as lightweight fillers and blowing agents. Expandable mic...

Nanjing Chemical Material Corp.

Search This Blog